LAP100.29A4
LAP100.29A4 is mainly used for sintered mechanical parts with good hardenability and high strength.
Pre-alloyed powders are water atomized steel powders with 0.85% Mo and 1.5% Mo often used as-sintered with additions of copper or nickel to make it possible for good surface hardening etc.

LAP100.29A4 is mainly used for sintered mechanical parts with good hardenability and high strength.

Pre-alloyed powders are water atomized steel powders with 0.85% Mo and 1.5% Mo often used as-sintered with additions of copper or nickel to make it possible for good surface hardening etc.


图片 18.png 

The high compressibility of atomized iron powder makes it a perfect choice for manufacturing pure iron or iron alloy parts with high tensile strength as well as high compressive strength. The Water atomized iron powder is mainly used in powder metallurgy for production of high strength machine parts. Water atomized iron powder may be mixed with graphite,  nickel powder, copper powder and other metal powders to provide specific properties to the final product. It is also mixed with some lubricant such as zinc stearate before compaction.

202003121530064060339.jpg


图片 19.png   图片 7.png


Specification of Atomized iron powder LAP100.29A4


Chemical Properties（%）Unit                                    Specification


MinMax
C%
0.01
Si%
0.05
Mn  %0.350.55
P%
0.020
S%
0.015
Ni%1.301.55
Mo%1.151.40
HL%
0.25
Physical Properties
Apparent densityg/cm32.903.20
Flow rates/50g
28.00
Green density 600Mpag/cm36.65
Particle size distribution（%）
180-212um%
1
150-180um%
10
45-150um%

-45um%1030


PROPERTIES

LAP100.29A1+0.80%C +0.80%Zn-st, condition: temperature1125℃, sintering time 30min.


图片 18_2.png


图片 12.png    图片 14_2.png    图片 16.png



PRODUCT PACKING

25kg/bag, 1000kg/bag, the package can be customized by buyer’s requirements.


图片 8.png  图片 163.png